Refractive Index |
nF (486nm) = 1.4631; nd (588nm) = 1.4585;
nC (656nm) = 1.4564 |
| |
Refliction Loss |
for two surfaces at 400nm - 7.1%; at 588nm – 6.8%; |
| |
Birefringence Constant |
3.54 nm/cm |
| |
Abbe Constant |
67.8 |
| |
Bubbles/inclusions |
None |
| |
Fluorescence |
Virtually fluorescence free |
| |
Impurity Content |
Total metallic impurities: less than 0.3 ppm |
| |
OH- Content |
< 0.2 ppm |
| |
Density |
2.201 g/cm3 |
| |
Coefficient of Expansion |
0.55 x 10-6/oC |
| |
Softening Point |
1600oC (2912oF) |
| |
Annealing Point |
1120oC (2048oF) |
| |
Strain Point |
1025oC (1877oF) |
| |
Max. Service Temperature |
950oC (1742oF) - continuous
1200oC (2192oF) - limited time |
| |
Dielectric Strength |
250-400 kV/cm at 20oC |
| |
Young's Modulus |
73 GPa at 25oC |
| |
Shear Modulus |
31 GPa at 25oC |
| |
Rupture Modulus |
50 MPa at 25oC |
| |
Bulk Modulus |
36.9 GPa at 25oC |
| |
Poisson Ratio |
0.17 at 25oC |
| |
Knoop Hardness |
500 kg/mm2 |
| |
Compressive Strength |
1.1 GPa |
| |
Tensile Strength |
50 MPa |
| |
Molecular Weight |
28.09 |
| |
Class/Structure |
Amorphous glass |
| |
Chemical Stability |
High resistance to water and acids (except hydrofluoric). |