Refractive Index |
nd = 1.51680; ne = 1.51872 |
|
Reflection Loss |
8.3% at 588nm (2 surfaces) |
|
Abbe Constant |
nd = 64.17; ne = 63.96 |
|
Principal Dispersion |
nF – nC = 0.008054 nF' - nC' = 0.008110 |
|
Density |
2.51 g/cm3 |
|
Thermal Conductivity |
1.114 W/(m*K) |
|
Specific Heat Capacity |
0.858 J/(g*K) |
|
Coefficient of Expansion |
a (-30/+70°C) = 7.1? 10-6/K a (20/300°C) = 8.3? 10-6/K |
|
Transformation Temperature, Tg |
557°C |
|
Temperature of the glass at a viscosity of 1013 dPa? s |
557°C |
|
Temperature of glass in at a viscosity of 107.6 dPa s |
719°C |
|
Elasticity Modulus |
82 x 103 N/mm² |
|
Poisson's Ratio |
0.206 |
|
Stress optical coefficient |
2.77 x 10-6 mm²/N |
|
Knoop hardness (0.1/20) |
610 |
|
Bubble class |
0 |
|
Climatic resistance |
2 |
|
Stain resistance |
0 |
|
Acid resistance |
1 |
|
Alkali resistance |
2.0 |
|
Phosphate resistance |
2.3 |
|
Melting Frequency |
I |