Crystal Class |
Hexagonal |
|
Molecular Weight |
60.06 |
|
Density |
2.635-2.660 g/cm3 at 289 K |
|
Dielectric Constant for 3x107 Hz at 295 K
|
35 microns |
|
parallel |
4.27 |
|
perpendicular |
4.34 |
|
Reflection Loss |
at 2.05 µm (2 surfaces) for o-ray – 8.3%; for e-ray – 8.5%; |
|
Melting Temperature |
1740 K |
|
Specific Heat |
0.17 cal/(g K) at 273 K |
|
Knoop Hardness |
741 kg/mm2 |
|
Transmission Range |
0.4 - 4.5 µm |
|
Debye Temperature |
470 K |
|
Thermal Conductivity |
|
|
at 20 K (parallel/perpendicular) |
720/370 W/(m K) |
|
at 194 K (parallel/perpendicular) |
20/10W/(m K) |
|
at 323 K (parallel/perpendicular) |
10.7/6.2W/(m K) |
|
Thermal Expansion |
|
|
parallel |
8.0 x 10-6 1/K at 273-253 K |
|
perpendicular |
13.4 x 10-6 1/K at 273-253 K |
|
Young's Modulus |
|
|
parallel |
97.2 GPa |
|
perpendicular |
76.5 GPa |
|
Bulk Modulus |
36.4 GPa |
|
Shear Modulus |
31.14 GPa |
|
Solubility in water |
None |
|
Bangap |
8.4 |