KCl晶體 |
|
|
OPTICAL |
|
|
Transmission Range |
0.21 to 20 microns |
|
Refractive Index |
1.45644 at 10 microns |
|
Reflection Loss |
6.8% at 10 µm (2 surfaces) |
|
Index of Absorption |
1.22 x 10-3 cm-1 at 2.7µm |
|
Restrahlen Peak |
63.1 microns |
|
dN/dT |
-33.2 x 10-6/°C |
|
|
|
PHYSICAL |
|
|
Density |
1.99 g/cm3 |
|
Melting Point |
776°C |
|
Thermal Conductivity |
6.53Wm-1K-1 at 322K |
|
Thermal Expansion |
36 x 10-6/K at 300K |
|
Hardness |
Knoop 7.2 <110>, 9.3 <100> with 200g |
|
Specific Heat Capacity |
690 J kg-1K-1 |
|
Dielectric Constant |
4.64 at 1MHz at 300K |
|
Young's Modulus (E) |
29.67 GPa |
|
Shear Modulus (G) |
6.24 GPa |
|
Bulk Modulus (K) |
17.36 GPa |
|
Elastic Coefficients |
C11 = 39.8 C12 = 6.2 C44 = 6.25 |
|
Apparent Elastic Limit |
2.3 MPa (330psi) |
|
Poisson Ratio |
0.216 |
CHEMICAL |
|
|
Solubility |
34.7g/100g water |
|
Molecular Weight |
74.55 |
|
Class/Structure |
Cubic FCC, NaCl, Fm3m, (100) cleavage | | |
|