OPTICAL |
|
|
Transmission Range |
0.37 to 13.5 microns |
|
Refractive Index |
2.20084 at 10 microns |
|
Reflection Loss |
26.2% at 10 µm (2 surfaces) |
|
Index of Absorption |
0.0006 cm-1 at 3.8 microns |
|
Restrahlen Peak |
30.5 microns |
|
dN/dT |
+38.7 x 10-6/°C at 3.39µm |
|
|
|
PHYSICAL |
|
|
Density |
4.09 g/cm3 |
|
Melting Point |
1765°C (dissociates about 700°C) |
|
Thermal Conductivity |
27.2 Wm-1K-1 at 298K |
|
Thermal Expansion |
6.5 x 10-6/°C at 273K |
|
Hardness |
Knoop 160 with 50g indenter |
|
Specific Heat Capacity |
515 J kg-1K-1 |
|
Dielectric Constant |
8 |
|
Young's Modulus (E) |
74.5 GPa |
|
Apparent Elastic Limit |
68.9 MPa (10,000psi) |
|
Poisson Ratio |
0.28 |
|
|
|
CHEMICAL |
|
|
Solubility |
0.001 g/100g water |
|
Molecular Weight |
144.33 |
|
Class/Structure |
HIP polycrystalline cubic, ZnS, F43m | | |
|